PP CO-POLYMER - Typical Characteristics
|
| Property |
Test Method |
Unit |
Typical Value* |
| Melt Flow Rate (2300C/2.16 kg) |
ASTM D1238 |
gm/10min |
0.3 |
| Melt Flow Rate (2300C/5.0 kg) |
ASTM D1238 |
gm/10min |
1 |
| Tensile Strength at Yield (50 mm/min) |
ASTM D638 |
MPa |
27 |
| Elongation at Yield (50 mm/min) |
ASTM D638 |
% |
14 |
| Elongation at Break (50 mm/min) |
ASTM D638 |
% |
>500 |
| Flexural Modulus (1% secant) |
ASTM D790A |
MPa |
850 |
| Notched Izod Impact Strength (230C) |
ASTM D256 |
J/m |
550 |
| Type of Break |
|
|
No Break |
| Vicat Softening Point |
ASTM D1525 |
0C |
130 |
| Heat Deflection Temperature (455 kPa) |
ASTM D648 |
0C |
92 |
| * Typical values, not to be taken as specification. All the mechanical properties as per ASTM D638 Type I specimen injection moulded in accordance with ASTM D4101 |