Sample Data-Articles
Weight Charts Rods
WEIGHT CHART OF NYLON SQUARE RODS |
 |
Standard Length 300mm, 1200mm, and 1500mm
| Sl. No | Size in MM | Size in Inch | Approx. Weight (Kg.) 300mm Length |
| 1 | 25.40 X 25.40 | 1" | 0.280 |
| 2 | 31.70 X 31.70 | 1-1/4" | 0.420 |
| 3 | 38.10 X 38.10 | 1-1/2" | 0.600 |
| 4 | 50.80 X 50.80 | 2" | 1.050 |
| 5 | 63.50 X 63.50 | 2-1/2" | 2.150 |
| 6 | 76.20 X 76.20 | 3" | 2.150 |
| 7 | 100.00 X 100.00 | 4" | 3.750 |
PVC Sheets
|
|||||
| Product | PVC Gray Sheet | ||||
| Specification | 3mm | ||||
| Standard | Q/BLD2008-01 | ||||
| Testing Date | 08/12/9 | ||||
| Testing Item | Technical Criteria | Testing Result | |||
| Density，g/cm3 | 1.60-1.65 | 1.64 | |||
| Tensile Strength，Mpa | In Length | ≥15 | 39 | ||
| In breadth | ≥12 | 31 | |||
| Notch Impact Strength，kJ/m2 | In Length | ≥2.0 | 9 | ||
| In breadth | 10 | ||||
| Vicat Softening Temperature, ℃ | ≥70 | 75.2 | |||
| Heat Shrinkage , % | In Length | -6.0—+6.0 | -8.1 | ||
| In breadth | -5.0—+5.0 | +2.5 | |||
Test Certificate
TEST CERTIFICATES |
NylonCAST NYLONOLYPROPYELENEPVC RODSPVC SHEETSHDPEPU - POLYURETHANEPOM - POLYACETAL |
Pom - Polyacetal (Test Certificate)
|
||||
| PROPERTY | ASTM | POM-POLYACETAL | ||
| Specific gravity | D792 | 1.41 | ||
| P.S.I. Tensile Strength | D638 | 8800 | ||
| % Elongation | D638 | 40.75 | ||
| P.S.I. Comprehensive Strength | D695 | 16000 (10% defl.) | ||
| Impact Strength(1/2x1/2 in. notched) | D256 | 1.0-1.5 (1/2x1/2inbar) | ||
| Hardness Rockwell | D785 | M78-M80 | ||
| 105 P.S.I. 730 F Flexural Modules | D790 | 3.75 | ||
| Coefficient of friction | -- | 0.18 | ||
| -104 cal sec cm3 C cm Thermal conductivity | C177 | 5.5 | ||
| Thermal expansion 105per 0C | D696 | 8.5 | ||
| Resistance to heat0C (Continuous) | -- | 800 C 1200 C |
||
| Ω - cm (23 0C50%) Volume resistivity | D257 | 10 x 1014 | ||
| 1/8 in thickness volts mil Dielectric strength | D149 | 500 (90mil) | ||
| 1 KHz Dielectric constant | D150 | 3.7 | ||
| 1 KHz Dissipation (power) factor | D150 | 0.0010 (40mil) | ||
| 24/j3.2 mm % water absorption 24hr. 3.2 thickness, % | D150 | 0.22 | ||
| in mm Burning rate | D570 | 1.0 - 1.1 | ||
| Effect of weak acids | D635 | Resistant to some | ||
| Effect of strong acids | D543 | Attacked | ||
| Effect of weak alkalies | D543 | Attacked | ||
| Effect of strong alkalies | D543 | Attacked | ||
| Effect of organic solvents | D543 | Excellent resistance to practically all solvents. | ||
PU-Polyurethane (Test Certificate)
|
|||||
| PHYSICAL PROPERTIES (Based on MOCA curative) | |||||
| Hardness (Shore A) | 85 + 3 | 90 + 3 | 95 + 3 | ||
| Tensile Strength / psi (MPa) | 3045 (21.0) | 3620 (25.0) | 4060 (28.0) | ||
| 100% Modules / psi (MPa) | 700 (4.8) | 900 (6.2) | 900 (6.2) | ||
| 300% Modules / psi (MPa) | 1300 (9.0) | 1000 (11.7) | 2500 (17.2) | ||
| Angle Tear Strength (DIE C) (kN/m) | 66 | 77 | 98 | ||
| Elongation (%) | 550 | 450 | 430 | ||
| Compression set (22 hours @ 70C0) (%) | 45 | 45 | 50 | ||
| Cured Density (g/cm3) | 1.1 | 1.1 | 1.1 | ||